Si-TPV 3400-55A e ka tlamahano e ntle haholo ho TPE le likaroloana tse tšoanang tsa polar joalo ka PP, PA, PE, PS, joalo-joalo ...
Elongation at Break | 578% | ISO 37 |
Matla a tšepe | 6.0 Mpa | ISO 37 |
Shore A Hardness | 55 | ISO 48-4 |
Botenya | 1.1g/cm3 | ISO 1183 |
Matla a Kgapha | 33kN/m | ISO 34-1 |
Modulus ea Elasticity | 4.41 Mpa | |
MI(190℃,10KG) | 13.6 | |
Qhibiliha Mocheso Optimum | 220 ℃ | |
Mold Mocheso Optimum | 25 ℃ |
● Ho etsa ente ka ho toba.
● Tataiso ea Ts'ebetso ea Ente ea Mold
Nako ea ho omisa | 2-4 lihora |
Ho omisa Mocheso | 60-80 ℃ |
Feed Zone Temperature | 180-190 ℃ |
Mocheso oa Sebaka sa Bohareng | 190-200 ℃ |
Mocheso oa Sebaka sa Pele | 200-220 ℃ |
Mocheso oa Nozzle | 210-230 ℃ |
Qhibiliha Mocheso | 220 ℃ |
Mocheso oa hlobo | 20-40 ℃ |
Lebelo la Ente | Med |
Maemo ana a ts'ebetso a ka fapana ho ea ka lisebelisoa le mekhoa ea motho ka mong.
● Tšebetso ea Bobeli
Joalo ka thepa ea thermoplastic, thepa ea Si-TPV e ka sebetsoa ka bobeli bakeng sa lihlahisoa tse tloaelehileng
● Ente Molding Khatello
Khatello ea ho tšoara haholo e itšetlehile ka geometry, botenya le sebaka sa heke ea sehlahisoa. Khatello ea ho ts'oara e lokela ho behoa ho boleng bo tlaase qalong, 'me butle-butle e eketsehe ho fihlela ho se na mefokolo e amanang le sehlahisoa se entsoeng ka ente. Ka lebaka la thepa ea rekere ea thepa, khatello e feteletseng ea ho tšoara e ka baka deformation e tebileng ea karolo ea heke ea sehlahisoa.
● Khatello ea mokokotlo
Ho kgothaletswa hore khatello e ka morao ha screw e khutlisetsoa morao e lokela ho ba 0.7-1.4Mpa, e ke keng ea netefatsa feela ho tšoana ha ho qhibiliha ho qhibiliha, empa hape ho netefatsa hore thepa ha e senyehe haholo ke ho kuta. Lebelo le khothaletsoang la screw ea Si-TPV ke 100-150rpm ho netefatsa ho qhibiliha ho felletseng le polasetiki ea thepa ntle le ho senyeha ha thepa ho bakoang ke ho futhumatsa ha shear.
1. Lihlahisoa tsa Si-TPV elastomer li ka etsoa ho sebelisoa mekhoa e tloaelehileng ea tlhahiso ea thermoplastic, ho kenyelletsa le overmolding kapa co-molding le substrates tsa polasetiki tse kang PP,PA.
2. Maikutlo a silky ka ho fetisisa a Si-TPV elastomer ha a hloke mehato e eketsehileng ea ho sebetsa kapa ea ho roala.
3. Maemo a ts'ebetso a ka fapana ka lisebelisoa le mekhoa ea motho ka mong.
4. Ho omisoa ha desiccant desiccant dehumidifying ho kgothaletswa bakeng sa ho omisa hohle.
25KG / mokotla, mokotla oa pampiri oa matsoho o nang le mokotla o ka hare oa PE.
Lipalangoang joalo ka lik'hemik'hale tse seng kotsi. Boloka sebakeng se phodileng le se nang le moya o motle.
Litšobotsi tsa mantlha li lula li sa fetohe bakeng sa likhoeli tse 12 ho tloha ka letsatsi la tlhahiso haeba li bolokiloe sebakeng se khothaletsoang.